Mechanical properties:
the first group of mechanical properties according to GOST 3282-74, the second group of mechanical properties according to GOST 3282-74

Mechanical properties:
the first group of mechanical properties according to GOST 3282-74, the second group of mechanical properties according to GOST 3282-74

Weight, kg: 700—2000 coils

Weight, kg: 700—2000 coils

Weight, kg: 700—2000 coils

Weight, kg: 200—900 Rosettes

Weight, kg: 700—2000 coils

Weight, kg:
1.0-1.3 mm — 100—150, 300—450, 700—900 Rosettes;
1.4-6.0 mm — 100—150 700—900 Rosettes;

Weight, kg:
1.0-1.3 mm — 100—150, 300—450, 700—900 Rosettes;
1.4-6.0 мм — 100—150 700—900 Rosettes;

Used for welding low-carbon and low-alloyed steels in shielding blends, carbon dioxide and in submerged arc welding. High-purity surface of copper-coated and polished wire, precision layers winding, uniform cross -section along its whole length combined with low content of impurities, such as sulfur and phosphorous, provide for high productivity and improvement of welding-technological properties: low spatter, low rippling during weld formation. Mechanical properties of all-weld metal, that satisfy the most stringent requirements set by the industry regulatory documents, are ensured by optimum ratio of alloying elements. All-weld metal is resistant to crack-formation; has high impact strength values at temperatures up to - 60°С. All factors, that ensure continuous and smooth feedability, are accounted for in the production of wire: copper-coating quality, helix, limit deviations of wire diameter, precision layers winding.

APPROVED BY CERTIFYING BODIES:

NAKs – TU 24.34.13-003-93827560-2020, GOST 2246, ГДО, ГО, КО, МО, НГДО, ОТОГ, ОХНВП, ПТО, СК, КСМ.
RMRS – TУ 1227-006-93827560-2019
RRR – TU 1227-004-93827560-2019 VNIIJT No2332/02СВМ-07018/20/1
VNIIJT No2333/02СВМ-07018/20/2
NIC «Kurchatovskiy InstiTUtE - CNII KM Prometey

Used for welding low-carbon and low-alloyed steels in shielding blends, carbon dioxide and in submerged arc welding. High-purity surface of copper-coated and polished wire, precision layers winding, uniform cross -section along its whole length combined with low content of impurities, such as sulfur and phosphorous, provide for high productivity and improvement of welding-technological properties: low spatter, low rippling during weld formation. Mechanical properties of all-weld metal, that satisfy the most stringent requirements set by the industry regulatory documents, are ensured by optimum ratio of alloying elements. All-weld metal is resistant to crack-formation; has high impact strength values at temperatures up to - 60°С. All factors, that ensure continuous and smooth feedability, are accounted for in the production of wire: copper-coating quality, helix, limit deviations of wire diameter, precision layers winding.

APPROVED BY CERTIFYING BODIES:

NAKs – TU 24.34.13-003-93827560-2020, GOST 2246, ГДО, ГО, КО, МО, НГДО, ОТОГ, ОХНВП, ПТО, СК, КСМ.
RMRS – TУ 1227-006-93827560-2019
RRR – TU 1227-004-93827560-2019 VNIIJT No2332/02СВМ-07018/20/1
VNIIJT No2333/02СВМ-07018/20/2
NIC «Kurchatovskiy InstiTUtE - CNII KM Prometey

Used for welding low-carbon and low-alloyed steels in shielding blends, carbon dioxide and in submerged arc welding. High-purity surface of copper-coated and polished wire, precision layers winding, uniform cross -section along its whole length combined with low content of impurities, such as sulfur and phosphorous, provide for high productivity and improvement of welding-technological properties: low spatter, low rippling during weld formation. Mechanical properties of all-weld metal, that satisfy the most stringent requirements set by the industry regulatory documents, are ensured by optimum ratio of alloying elements. All-weld metal is resistant to crack-formation; has high impact strength values at temperatures up to - 60°С. All factors, that ensure continuous and smooth feedability, are accounted for in the production of wire: copper-coating quality, helix, limit deviations of wire diameter, precision layers winding.

APPROVED BY CERTIFYING BODIES:

NAKs – TU 24.34.13-003-93827560-2020, GOST 2246, ГДО, ГО, КО, МО, НГДО, ОТОГ, ОХНВП, ПТО, СК, КСМ.
RMRS – TУ 1227-006-93827560-2019
RRR – TU 1227-004-93827560-2019 VNIIJT No2332/02СВМ-07018/20/1
VNIIJT No2333/02СВМ-07018/20/2
NIC «Kurchatovskiy Institute - CNII KM Prometey

Used for welding low-carbon and low-alloyed steels in shielding blends and carbon dioxide.High-purity surface of copper-coated and polished wire, precision layers winding, uniform cross -section along its whole length combined with low content of impurities, such as sulfur and phosphorous, provide for high productivity and improvement of welding-technological properties: low spatter, low rippling during weld formation. Mechanical properties of all-weld metal, that satisfy the most stringent requirements set by the industry regulatory documents, are ensured by optimum ratio of alloying elements. All-weld metal is resistant to crack-formation; has high impact strength values at temperatures up to - 60°С. All factors, that ensure continuous and smooth feedability, are accounted for in the production of wire: copper-coating quality, helix, limit deviations of wire diameter, precision layers winding.

APPROVED BY CERTIFYING BODIES:

NAKS – TU 24.34.13-007-93827560-2020 ГДО, ГО, КО, МО, НГДО, ОТОГ, ОХНВП, ПТО, СК
TU 1227-00793827560-2020

Used for welding low-carbon and low-alloyed steels in shielding blends and carbon dioxide.High-purity surface of copper-coated and polished wire, precision layers winding, uniform cross -section along its whole length combined with low content of impurities, such as sulfur and phosphorous, provide for high productivity and improvement of welding-technological properties: low spatter, low rippling during weld formation. Mechanical properties of all-weld metal, that satisfy the most stringent requirements set by the industry regulatory documents, are ensured by optimum ratio of alloying elements. All-weld metal is resistant to crack-formation; has high impact strength values at temperatures up to - 60°С. All factors, that ensure continuous and smooth feedability, are accounted for in the production of wire: copper-coating quality, helix, limit deviations of wire diameter, precision layers winding.

APPROVED BY CERTIFYING BODIES:

NAKS – TU 24.34.13-007-93827560-2020 ГДО, ГО, КО, МО, НГДО, ОТОГ, ОХНВП, ПТО, СК
TU 1227-00793827560-2020

Welding wire Св-08А, Св-08АА belongs to the low-carbon Class of wires with low content of impurities such as phosphorous and sulfur. Wire is intended for welding of low-carbon and low-alloyed steels. Carbon content in Св-08А, Св-08АА wire is ≤ 0,10 %. No alloying additives. Used at automatic and semi-automatic welding machines. Св-08А, Св-08АА wire of large diameters used for electrode production. Welding wire can have copper-coated or polished surface. Welding with Св-08А, Св-08АА wire produces straight and durable welding seam. This welding wire creates a relatively low level of spatter. Welding seam exhibits good characteristics for tensile testing and impact testing at negative temperatures. Wire Св-08А, Св-08АА allows to be applied at welding machine of any type. Used for submerged or gas-shielded welding. Welding, when using wire Св-08А, Св-08АА as consumable electrode, is performed at reversed polarity. Welding at direct polarity accelerates metal melting by about 1,5 times, though it will lower arc stability and increase spatter. Current depends on diameter and welding type. Welding with carbon dioxide exhibits high performance and relatively low cost since argon is much more expensive than carbon dioxide.

APPROVED BY CERTIFYING BODIES:

NAKS – TU 24.34.13-007-93827560-2020, GOST 2246
TU: ГДО, ГО, КО, МО, НГДО, ОТОГ, ОХНВП, ПТО, СК

Welding wire Св-08А, Св-08АА belongs to the low-carbon Class of wires with low content of impurities such as phosphorous and sulfur. Wire is intended for welding of low-carbon and low-alloyed steels. Carbon content in Св-08А, Св-08АА wire is ≤ 0,10 %. No alloying additives. Used at automatic and semi-automatic welding machines. Св-08А, Св-08АА wire of large diameters used for electrode production. Welding wire can have copper-coated or polished surface. Welding with Св-08А, Св-08АА wire produces straight and durable welding seam. This welding wire creates a relatively low level of spatter. Welding seam exhibits good characteristics for tensile testing and impact testing at negative temperatures. Wire Св-08А, Св-08АА allows to be applied at welding machine of any type. Used for submerged or gas-shielded welding. Welding, when using wire Св-08А, Св-08АА as consumable electrode, is performed at reversed polarity. Welding at direct polarity accelerates metal melting by about 1,5 times, though it will lower arc stability and increase spatter. Current depends on diameter and welding type. Welding with carbon dioxide exhibits high performance and relatively low cost since argon is much more expensive than carbon dioxide.

APPROVED BY CERTIFYING BODIES:

NAKS – TU 24.34.13-007-93827560-2020, GOST 2246
TU: ГДО, ГО, КО, МО, НГДО, ОТОГ, ОХНВП, ПТО, СК

Welding wire СВ-08ГА is intended for welding of carbon steels, such as 10 Low-alloyed steels for welded structures, in shielded gases or submerged. Used for welding in pipe manufacturing and power engineering industry, in manufacturing of oil-and-gas pipes of large cross-section made of low-alloyed steels, designed for high working pressure in extreme Artic environment. This welding wire creates a relatively low level of spatter. Welding seam exhibits good characteristics for tensile testing and impact testing at negative temperatures. All factors, that ensure continuous and smooth feedability, are accounted for in the production of wire: copper-coating quality, helix, limit deviations of wire diameter, precision layers winding.

APPROVED BY CERTIFYING BODIES:

NAKS – TU 24.34.13-007-93827560-2020, GOST 2246
TU: ГДО, ГО, КО, МО, НГДО, ОТОГ, ОХНВП, ПТО, СК
NAKS: TU 24.34.13-003-93827560-2020, GOST 2246-70
TU: ГДО, ГО, КО, МО, НГДО, ОТОГ, ОХНВП, ПТО, СК, КСМ

Welding wire СВ-08ГА is intended for welding of carbon steels, such as 10 Low-alloyed steels for welded structures, in shielded gases or submerged. Used for welding in pipe manufacturing and power engineering industry, in manufacturing of oil-and-gas pipes of large cross-section made of low-alloyed steels, designed for high working pressure in extreme Artic environment. This welding wire creates a relatively low level of spatter. Welding seam exhibits good characteristics for tensile testing and impact testing at negative temperatures. All factors, that ensure continuous and smooth feedability, are accounted for in the production of wire: copper-coating quality, helix, limit deviations of wire diameter, precision layers winding.

APPROVED BY CERTIFYING BODIES:

NAKS – TU 24.34.13-007-93827560-2020, GOST 2246
TU: ГДО, ГО, КО, МО, НГДО, ОТОГ, ОХНВП, ПТО, СК
NAKS: TU 24.34.13-003-93827560-2020, GOST 2246-70
TU: ГДО, ГО, КО, МО, НГДО, ОТОГ, ОХНВП, ПТО, СК, КСМ